SM ISO690:2012 MIHALACHE, Valentina, STEFAN, N., MIROIU, F.. CeO2 single buffer layer for YBCO RABiTS coated conductors. In: Moldavian Journal of the Physical Sciences, 2010, nr. 3-4(9), pp. 358-362. ISSN 1810-648X. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Moldavian Journal of the Physical Sciences | ||||||
Numărul 3-4(9) / 2010 / ISSN 1810-648X /ISSNe 2537-6365 | ||||||
|
||||||
Pag. 358-362 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
Chemical solution deposition techniques are promising approaches to achieve epitaxial
oxide thin films at a low cost and easy scaling for YBa2Cu3O7 coated conductors. High quality CeO2 buffer layers were prepared by CSD on Ni RABiTS. The precursor used for the
preparation of fluorite CeO2 films was Ce(III) acetate dissolved in propionic acid. YBCO layers were deposited by pulsed laser deposition (PLD) on CeO2 buffers, leading to a simple low
cost architecture NiRABiTS/CeO2 CSD/YBCOPLD. YBCO film epitaxially grown on 181-nm-
thick CeO2 buffer exhibited a critical temperature Tc = 90.5 K. Some aspects regarding the
correlation between the surface morphology of CeO2 film, the microstructure, and the transport parameters of YBCO film deposited on this buffer are discussed. |
||||||
|