SM ISO690:2012 GHITA, R., NEGRILA, Constantin, UNGUREANU, F., PREDOI, D.. Compositional and aspect studies of sulphur passivation on n-GaAs. In: Moldavian Journal of the Physical Sciences, 2010, nr. 3-4(9), pp. 270-274. ISSN 1810-648X. |
EXPORT metadate: Google Scholar Crossref CERIF DataCite Dublin Core |
Moldavian Journal of the Physical Sciences | ||||||
Numărul 3-4(9) / 2010 / ISSN 1810-648X /ISSNe 2537-6365 | ||||||
|
||||||
Pag. 270-274 | ||||||
|
||||||
Descarcă PDF | ||||||
Rezumat | ||||||
A real GaAs surface is covered with a relatively thick layer (~nm) of native oxide responsi-
ble for the surface Fermi level pinning within the band gap of the semiconductor. The method
presented in this work is the sulphur passivation by treating the semiconductor in sulphide solutions that combines both chemical and electronic passivation by reducing the surface state density
(e.g., pure ammonium sulphide and sulphur monochloride). The passivated surface was examined
by SEM, EDS and XPS techniques, that put into evidence the existence of an adherent layer of
sulphur compound as a result of chemical interaction of sulphur ions with n-GaAs surface.
|
||||||
|